Product manual
Reinforced 15% glass fiber reinforced material
General description
Material state Solid state
Exterior natural color
processing methods Injection molding
Stuffing glass fiber
form particle
Physical properties [1] Test method Test Conditions Unit Attribute value[2]
proportion ISO 1183 (23卤0.5)掳C g/cm3 1.231
Melt volume flow rate ISO 1133 275掳C/5.0kg cm3/10min 78
Mold shrinkage ISO 294-4 3.18mm % 0.5
Mechanical properties [1] Test method Test Conditions Unit Attribute value[2]
Tensile Strength ISO 527 5.0mm/min MPa 130
Elongation ISO 527 5.0mm/min % 3.5
Flexural modulus ISO 178 2mm/min MPa 5175
Thermal performance [1] Test method Test Conditions Unit Attribute value[2]
Heat distortion temperature ISO 75/A 1.80MPa,Unannealed 掳C 192
Impact performance [1] Test method Test Conditions Unit Attribute value[2]
Izod notched impact strength ASTM D256 (23卤3)掳C J/cm 60
Izod notched impact strength ASTM D256 -40掳C J/cm 46
Simply supported beam unnotched impact strength ISO 179 (23卤3)掳C kJ/m2 110
Simply supported beam unnotched impact strength ISO 179 -30掳C kJ/m2 45
Flammability [1] Test method Test Conditions Unit Attribute value[2]
UL flame retardant rating UL 94 1.5mm / HB
[1] The material properties of different colors will vary.
[2] The attribute values are for reference only, not as any technical indicators or technical agreements.
Nylon has good comprehensive properties. Compared with other engineering plastics, PA6 has the advantages of good mechanical properties, wear resistance and oil resistance. In recent years, with the rapid development of domestic and foreign automotive, electronic and electrical, communications and other industries, the proportion of PA6 applications has continued to increase. Among them, the proportion of applications in the vehicle transportation industry has reached 63%, and the proportion of applications in the electronic, electrical and office supplies industries has reached, The wide application of nylon products puts forward higher requirements for its performance, and the research on modification of its defects such as large water absorption, low elastic modulus and poor heat resistance, light resistance and low temperature impact resistance has been continuously developed. Wholesale PA6